Non Woven Flat Copper (Aluminum) Wire

PRODUCTION MODEL: WM(L)(B)-0.20~1.25。 This product is produced by extrusion process (flat) copper (aluminum) wire wrapped with 2-3 layers of polyester film and electrical non-woven fabric as insulation layer, with excellent voltage resistance. Suitable for manufacturing type reactors.

Products Details

Production Range

1. Cloth covered copper (aluminum) flat wire: Thickness size -- A: 0.80 ~ 5.60mm; Thickness size -- B: 2.00 ~ 16.00mm. 2. Cloth covered copper (aluminum) round wire -- D: 1.90 ~ 5.00mm.

Conducting Material 

1. The aluminum wire meets the requirements of GB/T 55843-2009, and the resistivity at 20℃ should be ≤0.02801 ω ·mm²/m; 2. The copper wire complies with the requirements of GB/T 55842-2009, and the resistivity at 20℃ should be less than or equal to 0.01724 ω ·mm²/m.

 Technical Parameter

Size of round conductor should comply with the following table:

Nominal Diameter

Deviation

0.90dspan=””2.50

±0.013

2.50dspan=”” 3.00

±0.025

3.00dspan=”” 5.00

±1%D

 Elongation of round conductor should comply with the following table:

Nominal Diameter

Min. Elongation %

0.90dspan=”” 2.50

15

2.50dspan=”” 5.00

20

 

Wide Application Of Electromagnetic Wire Coating Products

At present, the application of electromagnetic wire coating products has greatly increased the consumption of electromagnetic wire with the acceleration of the pace of China's modern industrial construction and the rapid growth of export products. The enameled wire and electromagnetic wire mainly use the insulating electrostatic powder coating. At present, they are mainly used in the insulating oxide film electromagnetic wire instead of the concentrated sulfuric acid treatment of aluminum wire, and can also be used in the enameled paint of insulating paint coating on-line. Because the coating thickness of general powder coating is applicable to the circular wire with the diameter of more than 1.6m m or the flat wire with the width of more than 1.6mm × 1.6mm, and the insulating coating with the thickness of more than 40 μ m, it is not applicable to the coating requiring thin coating. If the ultra-thin powder coating is used, the thickness of 20-40 μ M can be achieved. However, because of the cost of coating processing and the difficulty of coating, it can not be widely used. When the film thickness is too thick, the flexibility and other functions of the film are reduced, which is not suitable for products with too large bending angle of metal wire. Because of the limitation of film thickness, too thin wire is not suitable for powder coating technology.